Developed based on PA12; low water absorption, the size of printed parts is less affected by humidity and temperature. ePA12 has high toughness, high impact resistance, and can be used to print durable parts; it has up to 165% elongation at break and excellent fatigue resistance; self-lubricating wear resistance, can print mechanical gears; high temperature resistance, thermal deformation The temperature is 100℃, can be used for temperature-resistant parts; low shrinkage, not easy to warp and crack during printing.
Sellingpoint
Low moisture absorption
Heat resistance
High toughness
High impact resistance
Abrasion resistance
High dimensional stability
Excellent printability
3D PRINTING FILAMENT: ePA12
Density(g/cm3): 1.012
Heat Distortion Temp(℃,0.45MPa): 100
Melt Flow Index(g/10min): 55.64(270℃/2.16kg)
Tensile Strength(MPa): 50.81
Elongation at Break(%): 165.41
Flexural Strength(MPa): 47.27
Flexural Modulus(MPa): 659.49
IZOD Impact Strength(kJ/): 10.14
Durability: 10/10
Printability: 8/10
Recommended printing parameters
Extruder Temperature(℃): 260 – 290℃ Recommended temperature280℃
Bed temperature(℃): 70 – 90°C
Fan Speed: 0%
Printing Speed: 40 – 100mm/s
Heated Bed: Required
Recommended Build Surfaces: Solid glue, PEI
Feature
Flexible√
Elastic —
Impact Resistant√
Soft —
Composite —
UV Resistant —
Water Resistant —
Dissolvable —
Heat Resistant√
Chemically Resistant —
Fatigue Resistant√
Need drying√
Heated Bed Required√
Print recommend: Drying at 70℃/>12h